Quote:
Originally Posted by lordstanley13
Now that I think of it, It might of been too much pressure.... I do remember seeing the resin coming out of the crack by the break right after it happened... That would be one sign of too much pressure correct????
|
It would definately be a sign that a sub surface crack then turned into a surface crack. Sub surface cracks won't leak resin! Could too much stem or probe pressure cause that? Yes it could. Didn't answer my dry out question yet? Do you dry out repairs this time of year? If not, please start doing so because they all contain moisture.